本文主要研究内容
作者钟晓康,王幸福,韩福生（2019）在《316L不锈钢表面激光熔覆Stellite-F合金层的电化学腐蚀行为》一文中研究指出：采用CO2激光器在316L不锈钢表面熔覆Stellite-F合金,通过电化学方法研究了Stellite-F熔覆合金层在5wt%NaCl溶液中的腐蚀行为。结果表明:与316L不锈钢相比,与基材呈冶金结合的Stellite-F合金层自腐蚀电位较正、自腐蚀电流密度较小,无点腐蚀现象出现,耐海水腐蚀性能较好;研究发现,熔覆合金层物相主要由γ-Co固溶体与Ni3C、Cr23C6碳化物构成,在盐溶液中其腐蚀失效机制为选择性腐蚀,即固溶体合金相作为阳极被腐蚀浸出,碳化物相得到阴极保护暴露析出,同时固溶体相中的Co、Ni组分优先被腐蚀浸出,其余组分形成海绵状结构。
Abstract
cai yong CO2ji guang qi zai 316Lbu xiu gang biao mian rong fu Stellite-Fge jin ,tong guo dian hua xue fang fa yan jiu le Stellite-Frong fu ge jin ceng zai 5wt%NaClrong ye zhong de fu shi hang wei 。jie guo biao ming :yu 316Lbu xiu gang xiang bi ,yu ji cai cheng ye jin jie ge de Stellite-Fge jin ceng zi fu shi dian wei jiao zheng 、zi fu shi dian liu mi du jiao xiao ,mo dian fu shi xian xiang chu xian ,nai hai shui fu shi xing neng jiao hao ;yan jiu fa xian ,rong fu ge jin ceng wu xiang zhu yao you γ-Cogu rong ti yu Ni3C、Cr23C6tan hua wu gou cheng ,zai yan rong ye zhong ji fu shi shi xiao ji zhi wei shua ze xing fu shi ,ji gu rong ti ge jin xiang zuo wei yang ji bei fu shi jin chu ,tan hua wu xiang de dao yin ji bao hu bao lou xi chu ,tong shi gu rong ti xiang zhong de Co、Nizu fen you xian bei fu shi jin chu ,ji yu zu fen xing cheng hai mian zhuang jie gou 。
论文参考文献
论文详细介绍
论文作者分别是来自金属热处理的钟晓康,王幸福,韩福生，发表于刊物金属热处理2019年01期论文，是一篇关于不锈钢论文,激光熔覆论文,合金论文,电化学腐蚀论文,金属热处理2019年01期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自金属热处理2019年01期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。
标签：不锈钢论文; 激光熔覆论文; 合金论文; 电化学腐蚀论文; 金属热处理2019年01期论文;