作者杨文华,廖哲,郝花蕾,郝爱国,吉卫（2019）在《3A21铝合金锥形件旋压成形工艺》一文中研究指出：为了实现3A21铝合金小角度锥形件成形,采用多道次普强复合旋压和预成形后旋压两种工艺方法,研究了坯料尺寸、旋轮圆角半径、旋轮间隙等工艺参数对旋压结果的影响规律。结果表明,多道次普强复合旋压时,坯料相对厚度越小,减薄破裂、凸缘失稳起皱的趋势越明显;旋压后材料壁厚的变化呈U字形,两端厚,达到7 mm左右,中间薄,只有5 mm左右;贴模性较差,最大间隙达到0. 9 mm。通过预成形和剪切旋压相结合的方式,坯料不会产生失稳开裂的现象,壁厚控制更精确,得到旋压件侧壁的壁厚在7 mm左右,而口部的壁厚达到11 mm左右;旋压件贴模间隙很小,只有0. 2 mm左右。
Abstract
wei le shi xian 3A21lv ge jin xiao jiao du zhui xing jian cheng xing ,cai yong duo dao ci pu jiang fu ge xuan ya he yu cheng xing hou xuan ya liang chong gong yi fang fa ,yan jiu le pi liao che cun 、xuan lun yuan jiao ban jing 、xuan lun jian xi deng gong yi can shu dui xuan ya jie guo de ying xiang gui lv 。jie guo biao ming ,duo dao ci pu jiang fu ge xuan ya shi ,pi liao xiang dui hou du yue xiao ,jian bao po lie 、tu yuan shi wen qi zhou de qu shi yue ming xian ;xuan ya hou cai liao bi hou de bian hua cheng Uzi xing ,liang duan hou ,da dao 7 mmzuo you ,zhong jian bao ,zhi you 5 mmzuo you ;tie mo xing jiao cha ,zui da jian xi da dao 0. 9 mm。tong guo yu cheng xing he jian qie xuan ya xiang jie ge de fang shi ,pi liao bu hui chan sheng shi wen kai lie de xian xiang ,bi hou kong zhi geng jing que ,de dao xuan ya jian ce bi de bi hou zai 7 mmzuo you ,er kou bu de bi hou da dao 11 mmzuo you ;xuan ya jian tie mo jian xi hen xiao ,zhi you 0. 2 mmzuo you 。
论文参考文献
论文详细介绍
论文作者分别是来自锻压技术的杨文华,廖哲,郝花蕾,郝爱国,吉卫，发表于刊物锻压技术2019年10期论文，是一篇关于旋压成形论文,锥形件论文,失稳论文,变间隙论文,减薄率论文,锻压技术2019年10期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自锻压技术2019年10期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。