本文主要研究内容
作者胡省义（2019）在《稀土金属镧与杂多酸掺杂改性TiO2的制备及光催化性能》一文中研究指出：由于Ti02具有较大的禁带宽度,光生载流子易复合,实际应用中易团聚等制约了其广泛的应用。本文通过水热法合成Ti02纳米粉体,探究不同水热条件对Ti02形貌和催化性能的影响;并通过稀土金属镧和硅钨酸改性Ti02,探究稀土金属镧和硅钨酸改性对Ti02的晶体结构、光谱吸收和光催化性能的影响;以甲基橙溶液降解体系评价其光催化性能,实验结果如下:采用水热法制备Ti02纳米粉体,考察钛酸四丁酯浓度、水热反应时间、水热反应温度、去离子水用量、煅烧时间和煅烧温度等工艺参数对合成Ti02纳米粉体形貌和光催化性能的影响。结果表明:制备的TiO2为锐钛矿型,纺锤形颗粒,长径在50 nm左右,直径在10～30 nm,光催化性能与P25基本一致。在此研究基础上,通过水热法制备出稀土金属镧掺杂改性的Ti02复合粉体材料。镧离子的掺杂使得Ti02晶格发生畸变,平均粒径尺寸减小,比表面积增加,Ti02的光催化性能也得到了提高。当La/Ti摩尔比值为1.25%时,甲基橙的降解率达到了95.2%。在镧离子掺杂的基础上,使用硅钨酸对镧离子掺杂的La-Ti02纳米复合材料进行表面修饰,通过浸渍法制备改性纳米复合材料La-Ti02/SiW12,考察了浸渍工艺和煅烧条件对复合粉体光谱吸收和光催化性能的影响。结果表明,硅钨酸的浸渍浓度在0.04 mol/L、煅烧温度在400℃时,复合粉体在可见光区的吸收强度增强,甲基橙的降解率达到了98%。
Abstract
you yu Ti02ju you jiao da de jin dai kuan du ,guang sheng zai liu zi yi fu ge ,shi ji ying yong zhong yi tuan ju deng zhi yao le ji an fan de ying yong 。ben wen tong guo shui re fa ge cheng Ti02na mi fen ti ,tan jiu bu tong shui re tiao jian dui Ti02xing mao he cui hua xing neng de ying xiang ;bing tong guo xi tu jin shu lan he gui wu suan gai xing Ti02,tan jiu xi tu jin shu lan he gui wu suan gai xing dui Ti02de jing ti jie gou 、guang pu xi shou he guang cui hua xing neng de ying xiang ;yi jia ji cheng rong ye jiang jie ti ji ping jia ji guang cui hua xing neng ,shi yan jie guo ru xia :cai yong shui re fa zhi bei Ti02na mi fen ti ,kao cha tai suan si ding zhi nong du 、shui re fan ying shi jian 、shui re fan ying wen du 、qu li zi shui yong liang 、duan shao shi jian he duan shao wen du deng gong yi can shu dui ge cheng Ti02na mi fen ti xing mao he guang cui hua xing neng de ying xiang 。jie guo biao ming :zhi bei de TiO2wei rui tai kuang xing ,fang chui xing ke li ,chang jing zai 50 nmzuo you ,zhi jing zai 10～30 nm,guang cui hua xing neng yu P25ji ben yi zhi 。zai ci yan jiu ji chu shang ,tong guo shui re fa zhi bei chu xi tu jin shu lan can za gai xing de Ti02fu ge fen ti cai liao 。lan li zi de can za shi de Ti02jing ge fa sheng ji bian ,ping jun li jing che cun jian xiao ,bi biao mian ji zeng jia ,Ti02de guang cui hua xing neng ye de dao le di gao 。dang La/Tima er bi zhi wei 1.25%shi ,jia ji cheng de jiang jie lv da dao le 95.2%。zai lan li zi can za de ji chu shang ,shi yong gui wu suan dui lan li zi can za de La-Ti02na mi fu ge cai liao jin hang biao mian xiu shi ,tong guo jin zi fa zhi bei gai xing na mi fu ge cai liao La-Ti02/SiW12,kao cha le jin zi gong yi he duan shao tiao jian dui fu ge fen ti guang pu xi shou he guang cui hua xing neng de ying xiang 。jie guo biao ming ,gui wu suan de jin zi nong du zai 0.04 mol/L、duan shao wen du zai 400℃shi ,fu ge fen ti zai ke jian guang ou de xi shou jiang du zeng jiang ,jia ji cheng de jiang jie lv da dao le 98%。
论文参考文献
论文详细介绍
论文作者分别是来自华东理工大学的胡省义，发表于刊物华东理工大学2019-07-16论文，是一篇关于纳米粉体论文,水热法论文,镧掺杂论文,硅钨酸论文,华东理工大学2019-07-16论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自华东理工大学2019-07-16论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。
标签：纳米粉体论文; 水热法论文; 镧掺杂论文; 硅钨酸论文; 华东理工大学2019-07-16论文;