作者邓平,孙晨,彭群家,韩恩厚,柯伟,焦治杰（2019）在《核用304不锈钢辐照促进应力腐蚀开裂研究》一文中研究指出：采用2 MeV质子束在360℃对国产核用304不锈钢试样进行了辐照实验,利用高温高压水环境的慢应变速率拉伸实验(SSRT)和SEM、EBSD、TEM等研究了核用304不锈钢辐照促进应力腐蚀开裂(IASCC)机理。结果表明,慢应变速率拉伸过程中辐照促进材料晶界和表面滑移台阶处形成应变集中,且其程度随辐照剂量增加而增加。滑移台阶穿过或终止于晶界,终止于晶界的台阶造成晶界处产生不连续滑移,易将位错传输到晶界,在晶界区域形成位错塞积和残余应变集中。而台阶不连续滑移的形成则受毗邻晶粒的Schmidt因子对的类型影响。另一方面,辐照促进晶界发生贫Cr富Ni元素偏析,其偏析程度随辐照剂量增加而增加。SSRT实验后辐照试样表面发生明显的沿晶应力腐蚀开裂,且裂纹数量随辐照剂量和外加应变增加而增加。同时,裂纹尖端区域发生明显晶界腐蚀,且氧化物宽度和长度随辐照剂量增加而增加。分析认为,辐照致晶界应变集中和元素偏析的协同作用造成材料变形行为和晶界腐蚀行为变化是IASCC发生的关键因素。
Abstract
cai yong 2 MeVzhi zi shu zai 360℃dui guo chan he yong 304bu xiu gang shi yang jin hang le fu zhao shi yan ,li yong gao wen gao ya shui huan jing de man ying bian su lv la shen shi yan (SSRT)he SEM、EBSD、TEMdeng yan jiu le he yong 304bu xiu gang fu zhao cu jin ying li fu shi kai lie (IASCC)ji li 。jie guo biao ming ,man ying bian su lv la shen guo cheng zhong fu zhao cu jin cai liao jing jie he biao mian hua yi tai jie chu xing cheng ying bian ji zhong ,ju ji cheng du sui fu zhao ji liang zeng jia er zeng jia 。hua yi tai jie chuan guo huo zhong zhi yu jing jie ,zhong zhi yu jing jie de tai jie zao cheng jing jie chu chan sheng bu lian xu hua yi ,yi jiang wei cuo chuan shu dao jing jie ,zai jing jie ou yu xing cheng wei cuo sai ji he can yu ying bian ji zhong 。er tai jie bu lian xu hua yi de xing cheng ze shou pi lin jing li de Schmidtyin zi dui de lei xing ying xiang 。ling yi fang mian ,fu zhao cu jin jing jie fa sheng pin Crfu Niyuan su pian xi ,ji pian xi cheng du sui fu zhao ji liang zeng jia er zeng jia 。SSRTshi yan hou fu zhao shi yang biao mian fa sheng ming xian de yan jing ying li fu shi kai lie ,ju lie wen shu liang sui fu zhao ji liang he wai jia ying bian zeng jia er zeng jia 。tong shi ,lie wen jian duan ou yu fa sheng ming xian jing jie fu shi ,ju yang hua wu kuan du he chang du sui fu zhao ji liang zeng jia er zeng jia 。fen xi ren wei ,fu zhao zhi jing jie ying bian ji zhong he yuan su pian xi de xie tong zuo yong zao cheng cai liao bian xing hang wei he jing jie fu shi hang wei bian hua shi IASCCfa sheng de guan jian yin su 。
论文参考文献
论文详细介绍
论文作者分别是来自金属学报的邓平,孙晨,彭群家,韩恩厚,柯伟,焦治杰，发表于刊物金属学报2019年03期论文，是一篇关于核用不锈钢论文,质子辐照论文,局部变形论文,腐蚀论文,辐照促进应力腐蚀开裂论文,金属学报2019年03期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自金属学报2019年03期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。
标签：核用不锈钢论文; 质子辐照论文; 局部变形论文; 腐蚀论文; 辐照促进应力腐蚀开裂论文; 金属学报2019年03期论文;