本文主要研究内容
作者李斌,王萍（2019）在《ZrO2纳米粉对Al-Si合金微弧氧化陶瓷层组织和性能的影响》一文中研究指出：为提高铝硅合金在高温环境下的服役寿命,文中通过微弧氧化技术在硅酸盐体系电解液中于Al-Si合金表面制备ZrO2-Al2O3陶瓷层。采用扫描电子显微镜和X射线衍射仪分别对陶瓷层进行了表面、截面形貌以及物相组成分析。利用涡流测厚仪测量不同ZrO2加入量的膜厚,分析ZrO2-Al2O3体系陶瓷层的生长速率,通过自制隔热装置对陶瓷层进行隔热性能测试。研究结果表明:Al2O3陶瓷层表面由许多胞状熔融物烧结而成,粗糙度较大,并分布着孔洞较大的放电通道,膜厚约10μm;ZrO2-Al2O3陶瓷层表面除了胞状熔融物还有细小的颗粒,粗糙度较小,且陶瓷层更加致密,膜层厚度达到25μm。两种体系陶瓷层均形成了Al2O3及SiO2相,且在15°～50°范围内出现"馒头包"现象,说明陶瓷层中有非晶成分,但ZrO2-Al2O3陶瓷层中衍射峰"馒头包"的现象更为严重,非晶成分含量更高,说明在微弧氧化过程中ZrO2纳米粉的加入有利于亚稳相γ?Al2O3的形成。陶瓷层生长速度研究结果表明,电解液中ZrO2的浓度越大,陶瓷层厚度越厚,生长速度先增大后减小。隔热性能测试结果显示,随ZrO2含量的增多,陶瓷层的隔热温度升高,ZrO2的加入对涂层的隔热起到增强的作用。
Abstract
wei di gao lv gui ge jin zai gao wen huan jing xia de fu yi shou ming ,wen zhong tong guo wei hu yang hua ji shu zai gui suan yan ti ji dian jie ye zhong yu Al-Sige jin biao mian zhi bei ZrO2-Al2O3tao ci ceng 。cai yong sao miao dian zi xian wei jing he Xshe xian yan she yi fen bie dui tao ci ceng jin hang le biao mian 、jie mian xing mao yi ji wu xiang zu cheng fen xi 。li yong guo liu ce hou yi ce liang bu tong ZrO2jia ru liang de mo hou ,fen xi ZrO2-Al2O3ti ji tao ci ceng de sheng chang su lv ,tong guo zi zhi ge re zhuang zhi dui tao ci ceng jin hang ge re xing neng ce shi 。yan jiu jie guo biao ming :Al2O3tao ci ceng biao mian you hu duo bao zhuang rong rong wu shao jie er cheng ,cu cao du jiao da ,bing fen bu zhao kong dong jiao da de fang dian tong dao ,mo hou yao 10μm;ZrO2-Al2O3tao ci ceng biao mian chu le bao zhuang rong rong wu hai you xi xiao de ke li ,cu cao du jiao xiao ,ju tao ci ceng geng jia zhi mi ,mo ceng hou du da dao 25μm。liang chong ti ji tao ci ceng jun xing cheng le Al2O3ji SiO2xiang ,ju zai 15°～50°fan wei nei chu xian "man tou bao "xian xiang ,shui ming tao ci ceng zhong you fei jing cheng fen ,dan ZrO2-Al2O3tao ci ceng zhong yan she feng "man tou bao "de xian xiang geng wei yan chong ,fei jing cheng fen han liang geng gao ,shui ming zai wei hu yang hua guo cheng zhong ZrO2na mi fen de jia ru you li yu ya wen xiang γ?Al2O3de xing cheng 。tao ci ceng sheng chang su du yan jiu jie guo biao ming ,dian jie ye zhong ZrO2de nong du yue da ,tao ci ceng hou du yue hou ,sheng chang su du xian zeng da hou jian xiao 。ge re xing neng ce shi jie guo xian shi ,sui ZrO2han liang de zeng duo ,tao ci ceng de ge re wen du sheng gao ,ZrO2de jia ru dui tu ceng de ge re qi dao zeng jiang de zuo yong 。
论文参考文献
论文详细介绍
论文作者分别是来自西安工业大学学报的李斌,王萍，发表于刊物西安工业大学学报2019年04期论文，是一篇关于合金论文,等离子体电解氧化论文,纳米粉论文,热防护性能论文,西安工业大学学报2019年04期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自西安工业大学学报2019年04期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。
标签：合金论文; 等离子体电解氧化论文; 纳米粉论文; 热防护性能论文; 西安工业大学学报2019年04期论文;