作者（2019）在《Solid solution evolution during mechanical alloying in Cu–Nb–Al compounds》一文中研究指出：This work concerns the structural evolution of Cu70Nb20Al10（at%） alloy processed by mechanical alloying using a planetary ball mill in air atmosphere for different times（4 to 200 h）. The morphological, structural, microstructural, and thermal behaviors of the alloy were investigated by scanning electron microscopy, energy-dispersive spectroscopy, X-ray diffraction, and differential scanning calorimetry. X-ray diffraction patterns were examined using the Rietveld refinement technique with the help of the MAUD software. A disordered FCC-Cu（Nb,Al） solid solution was formed after 8 h of milling. The crystallite size, microstrain, and lattice parameter were determined by the Rietveld method. With increasing milling time, the crystallite size of the final product—ternary-phase FCC-Cu（Nb,Al）—is refined to the nanometer scale, reaching 12 nm after 200 h. This crystallographic structure combines good mechanical strength and good ductility. An increase in microstrain and partial oxidation were also observed with increasing milling time.
Abstract
This work concerns the structural evolution of Cu70Nb20Al10（at%） alloy processed by mechanical alloying using a planetary ball mill in air atmosphere for different times（4 to 200 h）. The morphological, structural, microstructural, and thermal behaviors of the alloy were investigated by scanning electron microscopy, energy-dispersive spectroscopy, X-ray diffraction, and differential scanning calorimetry. X-ray diffraction patterns were examined using the Rietveld refinement technique with the help of the MAUD software. A disordered FCC-Cu（Nb,Al） solid solution was formed after 8 h of milling. The crystallite size, microstrain, and lattice parameter were determined by the Rietveld method. With increasing milling time, the crystallite size of the final product—ternary-phase FCC-Cu（Nb,Al）—is refined to the nanometer scale, reaching 12 nm after 200 h. This crystallographic structure combines good mechanical strength and good ductility. An increase in microstrain and partial oxidation were also observed with increasing milling time.
论文参考文献
论文详细介绍
论文作者分别是来自International Journal of Minerals Metallurgy and Materials的，发表于刊物International Journal of Minerals Metallurgy and Materials2019年09期论文，是一篇关于,International Journal of Minerals Metallurgy and Materials2019年09期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自International Journal of Minerals Metallurgy and Materials2019年09期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。
标签：International Journal of Minerals Metallurgy and Materials2019年09期论文;