作者谢飞燕,徐德康,陈鸿雁（2019）在《一种新的荧光粉材料Ca8MgLu（PO4）7:Dy3+的制备及发光特性》一文中研究指出：采用高温固相法合成一种黄色荧光粉Ca8MgLu（PO4）7:Dy3+,通过X线衍射（XRD）荧光光谱（PLE,PL）和荧光寿命研究Ca8MgLu（PO4）7:Dy3+的发光特性.在350 nm近紫外光激发下,荧光粉呈黄光发射,蓝光发射峰位于480 nm处(由4F9/2→6H15/2跃迁产生),黄光发射峰位于572 nm处(由4F9/2→6H13/2跃迁产生),以黄光发射为最强.监测572 nm最强发射峰,激发光谱覆盖300 500 nm,主激发峰位于350 nm. Ca8MgLu（PO4）7:Dy3+的热猝灭性能良好:在150℃下的发光强度积分是室温25℃的87. 37%.研究结果表明Ca8MgLu（PO4）7:Dy3+荧光粉材料有潜力应用于发光二极管（LED）中.
Abstract
cai yong gao wen gu xiang fa ge cheng yi chong huang se ying guang fen Ca8MgLu（PO4）7:Dy3+,tong guo Xxian yan she （XRD）ying guang guang pu （PLE,PL）he ying guang shou ming yan jiu Ca8MgLu（PO4）7:Dy3+de fa guang te xing .zai 350 nmjin zi wai guang ji fa xia ,ying guang fen cheng huang guang fa she ,lan guang fa she feng wei yu 480 nmchu (you 4F9/2→6H15/2yue qian chan sheng ),huang guang fa she feng wei yu 572 nmchu (you 4F9/2→6H13/2yue qian chan sheng ),yi huang guang fa she wei zui jiang .jian ce 572 nmzui jiang fa she feng ,ji fa guang pu fu gai 300 500 nm,zhu ji fa feng wei yu 350 nm. Ca8MgLu（PO4）7:Dy3+de re cu mie xing neng liang hao :zai 150℃xia de fa guang jiang du ji fen shi shi wen 25℃de 87. 37%.yan jiu jie guo biao ming Ca8MgLu（PO4）7:Dy3+ying guang fen cai liao you qian li ying yong yu fa guang er ji guan （LED）zhong .
论文参考文献
论文详细介绍
论文作者分别是来自湖北大学学报(自然科学版)的谢飞燕,徐德康,陈鸿雁，发表于刊物湖北大学学报(自然科学版)2019年05期论文，是一篇关于荧光粉论文,白光论文,发光特性论文,湖北大学学报(自然科学版)2019年05期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自湖北大学学报(自然科学版)2019年05期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。
标签：荧光粉论文; 白光论文; 发光特性论文; 湖北大学学报(自然科学版)2019年05期论文;