本文主要研究内容
作者张君平,时振明,刘亚丽（2019）在《Q345E钢Φ140mm材晶粒度对-40℃冲击功的影响及轧制工艺改进》一文中研究指出：试验的Q345E钢(/%:0.13C,0.23Si,1.45Mn,0.012P,0.005S,0.045V,0.030Nb,0.030Al)的冶炼工艺为100 t EAF-LF-VD-Φ500 mm坯连铸-Φ140 mm材轧制。通过Q345E钢热处理试验得出晶粒度级别对试验钢-40℃冲击功有显著影响;当钢材晶粒度级别为7.0时,-40℃冲击功仅为12～16 J,当晶粒度级别为9.0～10.0时,-40℃冲击功为80～198 J。通过将终轧温度从960℃降至865～910℃,钢材晶粒度级别由7.0提高至8.5～9.6,-40℃冲击功由12～16 J提高到61～82 J,满足-40℃冲击功34 J的标准要求。
Abstract
shi yan de Q345Egang (/%:0.13C,0.23Si,1.45Mn,0.012P,0.005S,0.045V,0.030Nb,0.030Al)de ye lian gong yi wei 100 t EAF-LF-VD-Φ500 mmpi lian zhu -Φ140 mmcai ga zhi 。tong guo Q345Egang re chu li shi yan de chu jing li du ji bie dui shi yan gang -40℃chong ji gong you xian zhe ying xiang ;dang gang cai jing li du ji bie wei 7.0shi ,-40℃chong ji gong jin wei 12～16 J,dang jing li du ji bie wei 9.0～10.0shi ,-40℃chong ji gong wei 80～198 J。tong guo jiang zhong ga wen du cong 960℃jiang zhi 865～910℃,gang cai jing li du ji bie you 7.0di gao zhi 8.5～9.6,-40℃chong ji gong you 12～16 Jdi gao dao 61～82 J,man zu -40℃chong ji gong 34 Jde biao zhun yao qiu 。
论文参考文献
论文详细介绍
论文作者分别是来自特殊钢的张君平,时振明,刘亚丽，发表于刊物特殊钢2019年03期论文，是一篇关于棒材论文,冲击功论文,晶粒度论文,控轧控冷论文,特殊钢2019年03期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自特殊钢2019年03期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。
标签：棒材论文; 冲击功论文; 晶粒度论文; 控轧控冷论文; 特殊钢2019年03期论文;