作者张冠峰,任凤章,陈静静,张少鹏,王宇飞,熊毅（2019）在《30CrMnSi钢斗齿锻造组织和性能研究》一文中研究指出：某30CrMnSi钢斗齿的生产工艺为锻造成形及锻造余热淬火,对斗齿切割后进行了硬度检测,并在斗齿尾部(使用中易断裂部位)截取冲击试样进行试验,观察断口形貌及微观组织,探讨锻造工艺及热处理工艺对斗齿力学性能及组织的影响。结果表明:30CrMnSi钢锻造斗齿各部位的硬度和冲击功并不相同,齿顶尖处和靠近凹坑处硬度较低,凹坑侧壁冲击功明显低于尾部上边沿。其原因为斗齿终锻温度高,凹坑部位相对较为封闭,冷却条件较差,导致凹坑侧壁晶粒粗大,使该处的冲击功明显降低。
mou 30CrMnSigang dou chi de sheng chan gong yi wei duan zao cheng xing ji duan zao yu re cui huo ,dui dou chi qie ge hou jin hang le ying du jian ce ,bing zai dou chi wei bu (shi yong zhong yi duan lie bu wei )jie qu chong ji shi yang jin hang shi yan ,guan cha duan kou xing mao ji wei guan zu zhi ,tan tao duan zao gong yi ji re chu li gong yi dui dou chi li xue xing neng ji zu zhi de ying xiang 。jie guo biao ming :30CrMnSigang duan zao dou chi ge bu wei de ying du he chong ji gong bing bu xiang tong ,chi ding jian chu he kao jin ao keng chu ying du jiao di ,ao keng ce bi chong ji gong ming xian di yu wei bu shang bian yan 。ji yuan yin wei dou chi zhong duan wen du gao ,ao keng bu wei xiang dui jiao wei feng bi ,leng que tiao jian jiao cha ,dao zhi ao keng ce bi jing li cu da ,shi gai chu de chong ji gong ming xian jiang di 。
论文作者分别是来自热加工工艺的张冠峰,任凤章,陈静静,张少鹏,王宇飞,熊毅，发表于刊物热加工工艺2019年03期论文，是一篇关于锻造余热淬火论文,硬度论文,冲击功论文,热加工工艺2019年03期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自热加工工艺2019年03期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。
本文来源: https://www.lw50.cn/article/45d8fa482282f91449650b50.html