作者谢飞,程健,邹伟东,潘建伟（2019）在《交流电场对Q215钢800℃粉末法渗硼硼化物层生长的影响》一文中研究指出：与传统粉末法渗硼对比,研究交流电场对800℃不同渗剂条件下Q215钢渗硼层中FeB与Fe2B相生长的影响。结果表明:常规渗硼在渗剂硼铁含量低于3%、渗层未形成FeB时,增加硼铁可显著促进渗硼层生长;然后进一步增加硼铁含量,渗层出现FeB,但对渗层厚度影响不大。交流电场显著促进渗硼层生长,随硼铁含量的增加,渗层厚度先增后减。硼铁高于10%后,渗层才出现FeB。施加交流电场改善内扩散,可影响Fe2B、FeB生长和转化。
yu chuan tong fen mo fa shen peng dui bi ,yan jiu jiao liu dian chang dui 800℃bu tong shen ji tiao jian xia Q215gang shen peng ceng zhong FeByu Fe2Bxiang sheng chang de ying xiang 。jie guo biao ming :chang gui shen peng zai shen ji peng tie han liang di yu 3%、shen ceng wei xing cheng FeBshi ,zeng jia peng tie ke xian zhe cu jin shen peng ceng sheng chang ;ran hou jin yi bu zeng jia peng tie han liang ,shen ceng chu xian FeB,dan dui shen ceng hou du ying xiang bu da 。jiao liu dian chang xian zhe cu jin shen peng ceng sheng chang ,sui peng tie han liang de zeng jia ,shen ceng hou du xian zeng hou jian 。peng tie gao yu 10%hou ,shen ceng cai chu xian FeB。shi jia jiao liu dian chang gai shan nei kuo san ,ke ying xiang Fe2B、FeBsheng chang he zhuai hua 。
论文作者分别是来自热加工工艺的谢飞,程健,邹伟东,潘建伟，发表于刊物热加工工艺2019年14期论文，是一篇关于粉末法渗硼论文,交流电场论文,硼铁论文,热加工工艺2019年14期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自热加工工艺2019年14期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。
本文来源: https://www.lw50.cn/article/8922d127b8f3fbd740d16146.html