作者孟超（2019）在《车用轴盘铸件浇注系统设计与组织性能分析》一文中研究指出：采用3D打印铸型,对比分析了3种不同浇注工艺下ZL114A铝合金轴盘铸件的冶金质量。通过调整冷铁材质与降低浇注温度,实现了自下而上与自外向内的顺序凝固。结果表明,铸件满足铸件技术要求。轴盘铸件本体试样经T6和低温稳定化处理,平均抗拉强度、屈服强度与伸长率分别为340 MPa、260 MPa与6.5%。加入0.11%的Sb元素变质后,初生α-Al基体平均晶粒尺寸约为86μm,沿晶界分布的共晶Si相形貌为球形或椭圆形,T6态合金断口断裂机制为典型的韧窝断裂。
cai yong 3Dda yin zhu xing ,dui bi fen xi le 3chong bu tong jiao zhu gong yi xia ZL114Alv ge jin zhou pan zhu jian de ye jin zhi liang 。tong guo diao zheng leng tie cai zhi yu jiang di jiao zhu wen du ,shi xian le zi xia er shang yu zi wai xiang nei de shun xu ning gu 。jie guo biao ming ,zhu jian man zu zhu jian ji shu yao qiu 。zhou pan zhu jian ben ti shi yang jing T6he di wen wen ding hua chu li ,ping jun kang la jiang du 、qu fu jiang du yu shen chang lv fen bie wei 340 MPa、260 MPayu 6.5%。jia ru 0.11%de Sbyuan su bian zhi hou ,chu sheng α-Alji ti ping jun jing li che cun yao wei 86μm,yan jing jie fen bu de gong jing Sixiang xing mao wei qiu xing huo tuo yuan xing ,T6tai ge jin duan kou duan lie ji zhi wei dian xing de ren wo duan lie 。
论文作者分别是来自热加工工艺的孟超，发表于刊物热加工工艺2019年01期论文，是一篇关于铝合金论文,轴盘铸件论文,微观组织论文,力学性能论文,浇注系统论文,热加工工艺2019年01期论文的文章。本文可供学术参考使用，各位学者可以免费参考阅读下载，文章观点不代表本站观点，资料来自热加工工艺2019年01期论文网站，若本站收录的文献无意侵犯了您的著作版权，请联系我们删除。
本文来源: https://www.lw50.cn/article/d038a2a1e5cd4168898e1fba.html